Name | Composition | Microstructure | Typical Mechanical Property |
UPW-H | Fe-Cr-C | Austenite + Martensite Chromium carbide | 58-66 HRC |
UPW-H
Categories: Welding Consumables, Welding Electrode
Related products
-
UPW-801
Name Composition Microstructure Flux Typical Mechanical Property UPW-801 Fe-Ni-Mo Low alloy steel
(ferrite, bainite)UPW-888
(fused type)Hardness (3 layers ): 22 HRC
Tensile Strength: 760 MPa
Elongation: 25%Categories: Submerged Arc Wire, Welding Consumables -
UPW-812
牌號 化學成分 微結構 焊劑 典型熔金力學性能 UPW-852 Fe-Cr-Ni-Mo Martensite UPW-882
(sintered type)46-52 HRC Categories: Submerged Arc Wire, Welding Consumables -
UPW-814
Name Composition Microstructure Flux Typical Mechanical Property UPW-814 Fe-Cr-Ni-Mo Martensite
FerriteUPW-882
(sintered type)37-43 HRC Categories: Submerged Arc Wire, Welding Consumables -
UPW-803
Name Composition Microstructure Flux Typical Mechanical Property UPW-803 Fe-Cr-Mo-W-V Martensite UPW-882
(sintered)47-53 HRC Categories: Submerged Arc Wire, Welding Consumables