| 牌號 | 化學成分 | 微結構 | 焊劑 | 典型熔金力學性能 |
| UPW-852 | Fe-Cr-Ni-Mo | Martensite | UPW-882 (sintered type) | 46-52 HRC |

Related products
-

UPW-626
Name Composition Microstructure Typical Mechanical Property UPW-626 Fe-Cr-C Austenite + Martensite
Chromium carbide56-64 HRC Categories: Open Arc Flux Cored Wire, Welding Consumables -

UPW-801
Name Composition Microstructure Flux Typical Mechanical Property UPW-801 Fe-Ni-Mo Low alloy steel
(ferrite, bainite)UPW-888
(fused type)Hardness (3 layers ): 22 HRC
Tensile Strength: 760 MPa
Elongation: 25%Categories: Submerged Arc Wire, Welding Consumables -

UPW-628
Name Composition Microstructure Typical Mechanical Property UPW-628 Fe-Cr-Nb-C Austenite + Martensite
Chromium carbide
Niobium carbide62-68 HRC Categories: Open Arc Flux Cored Wire, Welding Consumables -

UPW-814
Name Composition Microstructure Flux Typical Mechanical Property UPW-814 Fe-Cr-Ni-Mo Martensite
FerriteUPW-882
(sintered type)37-43 HRC Categories: Submerged Arc Wire, Welding Consumables